Unidirectional warp cloths made of carbon fibre
Products from remaining stock: Carbon fibre-dry fabric
| RTM-resin-injection-process | Injectex G 1157 / EFP |
| Fibres | HTA |
| Primer | 5131 |
| Yarn | 6K |
| Weave | plain |
| Epoxy resin-binder | 5 % by weight (incl. primer) |
| Glass threads | 4 % by weight (11 g/m²) |
| Thickness of the warp cloths | 0,250 mm |
| Standard width of rolls | 1270 mm |
| Areal weight of the warp cloths | 291 g/m² (incl. binder + glass threads) |
| Areal weight of the fibres | 270 g/m² (incl. glass threads) |
Properties after curing with epoxy resin RTM 6:
| In warp direction | In fill direction (90°) | |
| Tensile strength | 1970 MPa | 67 MPa |
| Tensile modulus of elasticity |
136 GPa | 9,4 GPa |
| Compressive strength | 990 MPa | 240 MPa |